特性级别 | 透明级|||热稳定性|||导电级|||标准级|||高刚性||| |
牌号 | NA205-15 |
加工级别 | 注堕级|||涂覆级|||唰出级|||发泡级|||包覆||| |
品名 | LDPE |
厂家(产地) | 台湾亚聚 |
用途级别 | 管材级|||薄膜级|||照明灯具||| |
LDPE 台聚 NA205-15挤压淋膜等级
LDPE(低密度聚乙烯#高压聚乙烯)/NA205-15/聚合
用途: 其它
特性备注:挤压淋膜等级
重要参数: 熔体流动速率:3 g/10min 密度:0.923 g/cm3 缺口冲击强度:98 硬度:53 维卡软化点:100 ℃ 脆化温度:-76 ℃
生产厂商:聚合化学品股份有限公司
PAXOTHENE® NA205-15
低密度聚乙烯
USI Corporation
产品说明:
PAXOTHENE NA205-15 (LDPE) is specially developed for extrusion coating on various substrates such as paper, cellophane, aluminum foil, polyolefin film, polyester film and nylon film.
NA205-15 also possesses excellent adhesion to a variety of porous substrates such as paper as well as non-porous substrates such as cellophane and foil. Low moisture-vapor transmission rates in combination with excellent heat sealability makes NA205-15 a good coating material.
Concerning processability, good flow characteristics and low neck-in of NA205-15 provide high line speed and reduce the loss of resin in the extrusion coating.
附加功能
PDF物性文档 |
查找替代物 |
加入收藏 |
PAXOTHENE® NA205-15 物性表
基本信息 | |
---|---|
特性 |
|
用途 |
|
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
密度 | 0.919 | g/cm3 | ASTM D1505 |
熔流率(熔体流动速率) | 3.0 | g/10 min | ASTM D1238 |
硬度 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
肖氏硬度 (邵氏 D) | 53 | ASTM D2240 |
薄膜 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
抗张强度 | ASTM D882 | ||
MD : 屈服 | 9.02 | MPa | ASTM D882 |
TD : 屈服 | 9.02 | MPa | ASTM D882 |
MD : 断裂 | 19.1 | MPa | ASTM D882 |
TD : 断裂 | 15.4 | MPa | ASTM D882 |
伸长率 | ASTM D882 | ||
MD : 断裂 | 330 | % | ASTM D882 |
TD : 断裂 | 540 | % | ASTM D882 |
落锤冲击 | 98 | g | ASTM D1709 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
脆化温度 | < -76.0 | °C | ASTM D746 |
维卡软化温度 | 100 | °C | ASTM D1525 |
熔融峰值温度 | 109 | °C | ASTM D3418 |
光学性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
Gardner光泽度 (60°) | 100 | ASTM D523 | |
雾度 | 6.0 | % | ASTM D1003 |