| 品牌 | 亨斯迈 |
| 货号 | 236 |
| 用途 | 家用电器 |
| 牌号 | A92P4637 |
| 型号 | A92P4637 |
| 品名 | TPU |
| 外形尺寸 | 25kg |
| 生产企业 | 123 |
| 是否进口 |
良好的柔韧性TPU 亨斯迈 A92P4637
IROGRAN A 92 P 4637 is a thermoplastic polyether-polyurethane for injection moulding and extrusion applications.
Additional characteristics of the product are excellent microbial resistance, high low-temperature flexibility, especially suitable for cable jacket.
PERFORMANCE FEATURES
Excellent hydrolysis resistance
High microbial resistance
High stability of melt
Easy coloring
Low-temperature flexibility
APPLICATIONS
For the production of jacket material for cables, jackets for high pressure hosesspiral hoses, profiles.
IROGRAN® A 92 P 4637 物性表
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| Abrasion 2 | 30 | mm3 | ISO 4649 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 | ASTM D2240, ISO 868 | ||
| 邵氏 A, 注塑 | 92 | ASTM D2240, ISO 868 | |
| 邵氏 D, 注塑 | 39 | ASTM D2240, ISO 868 |
| 弹性体 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力 3 | |||
| 100%应变 | 8.96 | MPa | ASTM D412 |
| 100%应变 | 9.10 | MPa | DIN 53504 |
| 300%应变 | 14.1 | MPa | ASTM D412 |
| 300%应变 | 15.9 | MPa | DIN 53504 |
| 抗张强度 4 | |||
| 断裂 | 33.6 | MPa | ASTM D412 |
| 断裂 | 45.0 | MPa | DIN 53504 |
| 伸长率 5 | |||
| 断裂 | 670 | % | ASTM D412 |
| 断裂 | 600 | % | DIN 53504 |
| 撕裂强度 6 | |||
| -- | 116 | kN/m | ASTM D624 |
| -- | 74 | kN/m | ISO 34-1 |
| 压缩*变形 7 | ASTM D395, ISO 815 | ||
| 23°C, 24 hr | 25 | % | ASTM D395, ISO 815 |
| 70°C, 24 hr | 41 | % | ASTM D395, ISO 815 |
| 巴肖氏弹性 | 34 | % |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | |||
| -- | 100 到 110 | °C | |
| 真空干燥机 | 80.0 到 90.0 | °C | |
| 干燥时间 | |||
| -- | 3.0 | hr | |
| 真空干燥机 | 3.0 | hr | |
| Dew Point | -30.0 | °C | |
| 料筒后部温度 | 175 到 195 | °C | |
| 料筒中部温度 | 175 到 195 | °C | |
| 料筒前部温度 | 175 到 195 | °C | |
| 射嘴温度 | 180 到 200 | °C | |
| 加工（熔体）温度 | 170 到 195 | °C | |
| 模具温度 | 20.0 到 70.0 | °C |