LLDPE 卡塔尔石化 薄膜级 Q1018H
- 发布日期： 2018-05-15
- 更新日期： 2025-05-07
产品详请
| 特性级别 |
阻燃级|||增韧级|||透明级|||耐老化|||耐候|||高结晶（HCPP）|||高滑动|||
|
| 牌号 |
Q1018H
|
| 加工级别 |
中空级|||发泡级|||脱模级|||
|
| 品名 |
LLDPE
|
| 厂家(产地) |
卡塔尔石化
|
| 用途级别 |
填充级|||电子电器部件|||板材级|||照明灯具|||医用级|||
|
LLDPE 石化 薄膜级 Q1018H
Lotrène® LLDPE Q1018H
线性低密度聚乙烯
QATOFIN Company Limited
产品说明：
Lotrène® Q1018 Series are Linear Low Density Polyethylene resins produced in a gas phase reactor using butene (C4) co-monomer.
They are designed for blown film applications and can be used in pure form as well as blended with other PE resins, such as LDPE or HDPE and mPE resins for mono extrusion or co-extrusion process to modify film properties.
Lotrène® Q1018 Series are suited for many applications in the field of consumer, agricultural, industrial, food or hygiene packaging, for example: collation shrink, liners, FFS bags, heavy duty sacks,
refuse, tunnel films, mulching films…
Lotrène® LLDPE Q1018H 物性表
| 基本信息 |
|
|---|
| 添加剂 | 芥酸酰胺润滑添加剂 (1500 ppm) 抗结块剂 (3200 ppm) 热稳定剂
|
| 特性 | |
| 用途 | 包装 薄壁包装 薄膜 衬里 袋子 工业应用 混合 农业应用 食品包装 收缩性薄膜 消费品应用领域 重包装袋
|
| 加工方法 | |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 比重 | 0.918 | g/cm3 | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|
| 割线模量 |
|
| ASTM D882 |
| 1% 正割, MD : 40 μm, 吹塑薄膜 | 215 | MPa | ASTM D882 |
| 1% 正割, TD : 40 μm, 吹塑薄膜 | 245 | MPa | ASTM D882 |
| 抗张强度 |
|
| ASTM D882 |
| MD : 屈服, 40 μm, 吹塑薄膜 | 11.0 | MPa | ASTM D882 |
| TD : 屈服, 40 μm, 吹塑薄膜 | 11.0 | MPa | ASTM D882 |
| MD : 断裂, 40 μm, 吹塑薄膜 | 38.0 | MPa | ASTM D882 |
| TD : 断裂, 40 μm, 吹塑薄膜 | 33.0 | MPa | ASTM D882 |
| 伸长率 |
|
| ASTM D882 |
| MD : 断裂, 40 μm, 吹塑薄膜 | 800 | % | ASTM D882 |
| TD : 断裂, 40 μm, 吹塑薄膜 | 850 | % | ASTM D882 |
| 落锤冲击 1(40 μm, 吹塑薄膜) | 150 | g | ASTM D1709 |
| 埃尔曼多夫抗撕强度 |
|
| ASTM D1922 |
| MD : 40 μm, 吹塑薄膜 | 280 | g | ASTM D1922 |
| TD : 40 μm, 吹塑薄膜 | 480 | g | ASTM D1922 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 维卡软化温度 | 100 | °C | ASTM D1525 |
| 结晶峰温度 (DSC) | 122 | °C | 内部方法 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 光泽度 (45°, 40.0 μm, 吹塑薄膜) | 60 |
| ASTM D2457 |
| 雾度 (40.0 μm, 吹塑薄膜) | 11 | % | ASTM D1003 |
| 挤出 | 额定值 | 单位制 |
|
|---|
| 料筒1区温度 | 180 到 220 | °C |
|
| 料筒2区温度 | 180 到 220 | °C |
|
| 料筒3区温度 | 180 到 220 | °C |
|
| 料筒4区温度 | 180 到 220 | °C |
|
| 料筒5区温度 | 180 到 220 | °C |
|
| 熔体温度 | 200 | °C |
|
| 挤压说明 |
|---|
| Blow-up ratio: 2:1 to 3:1Die gap: >1.8 mm |