耐低温撞击PP 泰科纳 GF30-0453高强度
Material code according to ISO 1043-1: PP
Polypropylene reinforced with 30weight percent long
glass fibers. Low emission. The fibers are chemically coupled to the polypropylene
matrix. The pellets are cylindrical and normally as well as the
embedded fibers 10 mm long.
Parts molded of CELSTRAN have outstanding mechanical properties such
as high strength and stiffness combined with high heat deflection.
The notched impact strength is increased at elevated and low
temperatures due to the fiber skeleton built in the parts. The long
fiber reinforcement reduces creep significantly.
The very isotropic shrinkage in the molded parts minimizes the
warpage.
Complex parts can be manufactured with high reproducibility by
injection molding.
Application field: Functional/structural parts for automotive
Celstran® PP-GF30-0453 P10/10 物性表
| 基本信息 |
|
|---|---|
| 填料/增强材料 |
|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 形式 |
|
| 加工方法 |
|
| 树脂ID (ISO 1043) |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.12 | g/cm3 | ISO 1183 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 |
|
|
|
| -- | 7000 | MPa | ISO 527-2/1A/1 |
| 80°C | 4700 | MPa | ISO 527-2/1A |
| 拉伸应力 |
|
|
|
| 断裂 | 110 | MPa | ISO 527-2/1A/5 |
| 80°C | 70.0 | MPa | ISO 527-2/1A |
| 拉伸应变 |
|
|
|
| 断裂 | 2.2 | % | ISO 527-2/1A/5 |
| 断裂, 80°C | 2.3 | % | ISO 527-2/1A |
| 弯曲模量 |
|
|
ISO 178 |
| 23°C | 7000 | MPa | ISO 178 |
| 80°C | 6600 | MPa | ISO 178 |
| 弯曲应力 |
|
|
ISO 178 |
| 23°C | 180 | MPa | ISO 178 |
| 80°C | 100 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 |
|
|
ISO 179/1eA |
| -30°C | 22 | kJ/m2 | ISO 179/1eA |
| 23°C | 24 | kJ/m2 | ISO 179/1eA |
| 简支梁无缺口冲击强度 |
|
|
ISO 179/1eU |
| -30°C | 45 | kJ/m2 | ISO 179/1eU |
| 23°C | 55 | kJ/m2 | ISO 179/1eU |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 热变形温度 |
|
|
|
| 1.8 MPa, 未退火 | 155 | °C | ISO 75-2/A |
| 8.0 MPa, 未退火 | 122 | °C | ISO 75-2/C |
| 熔融温度 1 | 166 | °C | ISO 11357-3 |