| 品牌 | 杜邦 |
| 货号 | A1900 |
| 用途 | 100ST |
| 牌号 | |
| 型号 | A1900 |
| 品名 | POM |
| 外形尺寸 | 00.1 |
| 生产企业 | F10-03H |
| 是否进口 | 是 |
| 物理性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 模收缩 | 1.2-1.4 | % | |
| 比重 | 1.34 | ASTM D-792 | |
| 自燃性 | HB | UL-94 | |
| 吸水量 | ASTM D-570 | ||
| (50%相对湿度) | 0.35 | % | |
| (24小时浸渍) | 0.43 | % | |
| (浸渍平衡点) | 0.85 | % |
| 机械性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 拉伸强度 | ASTM D-638 | ||
| (100℃) | >17 | MPa | |
| (-55℃) | 99 | MPa | |
| IZOD冲击试验 (缺口-40℃) | 249 | j/m | ASTM D-256 |
| 挠曲系数 (100℃) | 340 | MPa | ASTM D-790 |
| 破裂点拉伸变形量 (122℃) | >480 | % | ASTM D-638 |
| 洛氏硬度M | 58 | ASTM D-785 | |
| 抗拉伸冲击强度 (长试片23℃) | 1590 | kj/m | ASTM D-1822 |
| 压缩应力 (23℃,10%变形) | 52 | MPa | ASTM D-695 |
| 洛氏硬度R | 105 | ASTM D-785 | |
| 挠曲系数 (-55℃) | 3260 | MPa | ASTM D-790 |
| 拉伸强度 (70℃) | >29 | MPa | ASTM D-638 |
| 破裂点拉伸变形量 (100℃) | >580 | % | ASTM D-638 |
| 挠曲系数 (122℃) | 230 | MPa | ASTM D-790 |
| 破裂点拉伸变形量 | ASTM D-638 | ||
| (70℃) | >498 | % | |
| (-55℃) | 455 | % | |
| IZOD冲击试验 (23℃) | 901 | j/m | ASTM D-256 |
| 抗剪强度 (23℃) | 34 | MPa | ASTM D-732 |
| 破裂点拉伸变形量 (23℃) | 521 | % | ASTM D-638 |
| 挠曲系数 | ASTM D-790 | ||
| (23℃) | 1280 | MPa | |
| (70℃) | 650 | MPa | |
| 压缩应力 (23℃,1%变形) | 8 | MPa | ASTM D-695 |
| 挠曲变形强度 (23℃) | 40 | MPa | ASTM D-790 |
| 挠曲疲劳忍耐限度 (50%RH,23℃,10周期) | 16 | MPa | ASTM D-671 |
| 拉伸强度 (23℃) | 64 | MPa | ASTM D-638 |
| 弹性系数 (23℃) | 1280 | MPa | ASTM D-638 |
| 拉伸强度 (122℃) | >11 | MPa | ASTM D-638 |
| 负载变形量 (140kg/cm,50℃) | 3.0 | % | ASTM D-621 |
| 电气性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 容积电阻率 (23℃,0.2%含水量) | 2.3×10 | Ω.cm | ASTM D-257 |
| 介电因数 (50%RH,23℃,10Hz) | 0.007 | ASTM D-150 | |
| 抗电弧 (3.1mm) | 120 | sec | ASTM D-495 |
| 介电强度 (瞬间Short time(2.3mm)) | 19.9(2.3) | kv/mm | ASTM D-149 |
| 介电常数 (50%RH,23℃,10-10Hz) | 4.1 | Ω.cm | ASTM D-150 |
| 热性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 热畸变温度 | ASTM D-648 | ||
| (0.5MPa) | 168 | ℃ | |
| (1.8MPa) | 65 | ℃ | |
| 线性热膨胀系数 | ASTM D-696 | ||
| (104-160℃) | 12.8 | 10-5m/m℃ | |
| (-40-29℃) | 9.9 | 10-5m/m℃ | |
| (60-104℃) | 9.7 | 10-5m/m℃ | |
| (29-60℃) | 10.6 | 10-5m/m℃ | |
| 熔点 | 175 | ℃ |