NORYL™ SE1GFN1 resin
聚苯醚 + PS
10% 玻璃纤维增强材料
SABIC Innovative Plastics
产品说明：
10% GR. UL94 V-1 rated. Halogen free flame retardant. Typical applications are TV chassis, deflection yokes and connectors.
NORYL™ SE1GFN1 resin 物性表
|
机械性能
|
额定值
|
单位制
|
测试方法
|
|
抗张强度 1(断裂)
|
74.5
|
MPa
|
ASTM D638
|
|
伸长率 2(断裂)
|
5.0
|
%
|
ASTM D638
|
|
弯曲模量 3(50.0 mm 跨距)
|
4000
|
MPa
|
ASTM D790
|
|
弯曲强度 4(断裂, 50.0 mm 跨距)
|
120
|
MPa
|
ASTM D790
|
|
冲击性能
|
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度
|
|
|
ASTM D256
|
|
-40°C
|
69
|
J/m
|
ASTM D256
|
|
23°C
|
96
|
J/m
|
ASTM D256
|
|
热性能
|
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度 (1.8 MPa, 未退火, 6.40 mm)
|
132
|
°C
|
ASTM D648
|
|
维卡软化温度
|
148
|
°C
|
ASTM D1525 5
|
|
RTI Elec
|
110
|
°C
|
UL 746
|
|
RTI Imp
|
105
|
°C
|
UL 746
|
|
RTI
|
110
|
°C
|
UL 746
|
|
电气性能
|
额定值
|
单位制
|
测试方法
|
|
体积电阻率
|
1.0E+15
|
ohms·cm
|
ASTM D257
|
|
介电常数
|
|
|
ASTM D150
|
|
50 Hz
|
3.00
|
|
ASTM D150
|
|
60 Hz
|
3.00
|
|
ASTM D150
|
|
1 MHz
|
3.00
|
|
ASTM D150
|
|
耗散因数
|
|
|
ASTM D150
|
|
50 Hz
|
1.7E-3
|
|
ASTM D150
|
|
60 Hz
|
1.7E-3
|
|
ASTM D150
|
|
1 MHz
|
1.6E-3
|
|
ASTM D150
|
|
相比耐漏电起痕指数(CTI)
|
PLC 2
|
|
UL 746
|
|
高电弧燃烧指数(HAI)
|
PLC 2
|
|
UL 746
|
|
高电压电弧起痕速率 (HVTR)
|
PLC 4
|
|
UL 746
|
|
热丝引燃 (HWI)
|
PLC 1
|
|
UL 746
|
|
可燃性
|
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级 (1.47 mm)
|
V-1
|
|
UL 94
|
|
极限氧指数
|
34
|
%
|
ASTM D2863
|
|
注射
|
额定值
|
单位制
|
|
|
干燥温度
|
104 到 110
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，
|
8.0
|
hr
|
|
|
|
0.020
|
%
|
|
|
建议注射量
|
30 到 70
|
%
|
|
|
料筒后部温度
|
249 到 299
|
°C
|
|
|
料筒中部温度
|
260 到 304
|
°C
|
|
|
料筒前部温度
|
271 到 310
|
°C
|
|
|
射嘴温度
|
282 到 310
|
°C
|
|
|
加工（熔体）温度
|
282 到 310
|
°C
|
|
|
模具温度
|
76.7 到 104
|
°C
|
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
|
螺杆转速
|
20 到 100
|
rpm
|
|