Nilit Nilamid A3 H G10 50% Glass Reinforced PA66
Polymer,Thermoplastic,Nylon,Nylon 66,Nylon 66, 50% Glass Fiber Filled
Nilit
产品说明:
Description: Nilamid A3 H G10 (50% Glass Reinforced) is a high strength material, that is used for structural applications. It is easy to mould, and shows outstanding stiffness and creep resistance, even at elevated temperatures. It is used for highly loaded applications like high torque transmission housings, electrical cable holders and tensioners of ski bindings.Key characteristics:
- High stiffness
- High strength
- Good impact strength
- Excellent thermal performance
- Good creep resistance
Information provided by NILIT.
Nilit Nilamid A3 H G10 50% Glass Reinforced PA66 物性表物理性能 额定值 (公制) 额定值 (英制) 测试方法 密度 1.57 g/cc 0.0567 lb/in3 ASTM D792, ISO 1183 吸水率 0.50 % 0.50 % 23°C, 24h in H<sub>2</sub>O; sim. ISO 62 饱和吸水率 3.5 % 3.5 % sim. ISO 62 线性成型收缩率,Flow 0.0020 cm/cm 0.0020 in/in Euronil 线性成型收缩率,横向 0.0030 cm/cm 0.0030 in/in Euronil 机械性能 额定值 (公制) 额定值 (英制) 测试方法 抗张强度(屈服) 220 MPa 31900 psi ISO 527, ASTM D638 伸长率 (断裂) 2.0 % 2.0 % ISO 527, ASTM D638 拉伸模量 16.5 GPa 2390 ksi ISO 527, ASTM D638 弯曲强度 310 MPa 45000 psi ISO 178, ASTM D790 230 MPa @Temperature 90.0 °C33400 psi @Temperature 194 °FISO 178, ASTM D790 弯曲模量 15.0 GPa 2180 ksi ISO 178, ASTM D790 9.50 GPa @Temperature 90.0 °C1380 ksi @Temperature 194 °FISO 178, ASTM D790 悬壁梁缺口冲击强度 13.0 kJ/m2 @Temperature -30.0 °C6.19 ft-lb/in2 @Temperature -22.0 °FISO 180/1A 16.0 kJ/m2 @Temperature 23.0 °C7.61 ft-lb/in2 @Temperature 73.4 °FISO 180/1A 简支梁无缺口冲击强度 7.00 J/cm2 33.3 ft-lb/in2 ISO 179 5.50 J/cm2 @Temperature -30.0 °C26.2 ft-lb/in2 @Temperature -22.0 °FISO 179 简支梁缺口冲击强度 1.60 J/cm2 7.61 ft-lb/in2 ISO 179 1.30 J/cm2 @Temperature -30.0 °C6.19 ft-lb/in2 @Temperature -22.0 °FISO 179 电气性能 额定值 (公制) 额定值 (英制) 测试方法 介电强度 22.0 kV/mm @Thickness 2.00 mm559 kV/in @Thickness 0.0787 inASTM D149 Comparative Tracking Index 350 V @Thickness 3.20 mm350 V @Thickness 0.126 inSol. B; IEC 112, UL 746A 500 V @Thickness 3.20 mm500 V @Thickness 0.126 inSol. A; IEC 112, UL 746A 热性能 额定值 (公制) 额定值 (英制) 测试方法 工作温度, Air 115 °C 239 °F 20,000 hr; IEC 216 载荷下热变形温度(0.46 MPa) 262 °C 504 °F ISO 75, ASTM D648 载荷下热变形温度(1.8 MPa) 257 °C 495 °F ISO 75, ASTM D648 维卡软化温度 257 °C 495 °F 49 N; ISO 306, ASTM D1525 260 °C 500 °F 9.8 N; ISO 306, ASTM D1525 可燃性(UL94) HB @Thickness 0.800 mmHB @Thickness 0.0315 inHB @Thickness 1.60 mmHB @Thickness 0.0630 inHB @Thickness 3.20 mmHB @Thickness 0.126 in极限氧指数 27 % 27 % ASTM D2863 灼热丝易燃指数 650 °C @Thickness 3.20 mm1200 °F @Thickness 0.126 inGlow Wire Flammability Index; IEC 694-2-12 650 °C @Thickness 0.800 mm1200 °F @Thickness 0.0315 inGlow Wire Flammability Index; IEC 694-2-12 加工性能 额定值 (公制) 额定值 (英制) 测试方法 射嘴温度 285 - 300 °C 545 - 572 °F 1区 270 - 290 °C 518 - 554 °F hopper 2区 275 - 290 °C 527 - 554 °F 3区 285 - 300 °C 545 - 572 °F 4区 285 - 300 °C 545 - 572 °F 加工(熔体)温度 280 - 300 °C 536 - 572 °F Do not melt above 300°C 模具温度 100 - 120 °C 212 - 248 °F Preferred 干燥温度 80.0 - 85.0 °C 176 - 185 °F 干燥时间 4 hour 4 hour 注射压力 70.0 - 100 MPa 10200 - 14500 psi 材料描述 测试方法 Clamping Force in tons, 0.7 times the projected surface area in cm2 Flammability Rating B28 FMVSS No. 302, 355x100x1 mm Heat Resistance - Ball Test OK at 125°C, IEC 309 OK at 165°C, IEC 309 Holding Pressure 90 Mpa