Nylacast POM C Acetal Copolymer

Acetal Copolymer, Unreinforced

Nylacast

产品说明：

The copolymer grade is the ideal combination of strength, stiffness and wears resistance. It absorbs very little moisture, is easily machinable and is genuinely porosity-free making it the preferred grade for food contact and medical applications. The product exhibits an elevated resistance to hydrolysis, strong alkalis and thermal-oxidative degradation when compared to acetal homopolymer.

Information provided by Nylacast Ltd.

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	1.41 g/cc	0.0509 lb/in3	method A; ISO 1183:1987
吸水率	0.20 % @Time 86400 sec	0.20 % @Time 24.0 hour	Immersion; ISO 62:1999
平衡吸湿	0.10 %	0.10 %	50%RH; ISO 62:1999
饱和吸水率	0.90 %	0.90 %	Immersion; ISO 62:1999

机械性能	额定值 (公制)	额定值 (英制)	测试方法
肖氏硬度 (邵氏 D)	85	85	ISO 868:2003
抗张强度(屈服)	70.0 MPa	10200 psi	Type 1B, 50mm/min; ISO 527-1/2:1993
伸长率 (断裂)	>= 15 %	>= 15 %	Type 1B, 50mm/min; ISO 527-1/2:1993
拉伸模量	2.70 GPa	392 ksi	Type 1B, 50mm/min; ISO 527-1/2:1993
弯曲强度	80.0 MPa	11600 psi	1.5mm/min; ISO 178:2001
弯曲模量	2.60 GPa	377 ksi	1.5mm/min; ISO 178:2001
抗压强度	110 MPa	16000 psi	Type B, 5mm/min; ISO 604:2002
压缩模量	2.60 GPa	377 ksi	Type B, 5mm/min; ISO 604:2002
悬壁梁缺口冲击强度	7.20 kJ/m2	3.43 ft-lb/in2	Type A; ISO 180:2000
动态摩擦系数	0.25 @Pressure 1.75 MPa	0.25 @Pressure 254 psi	31.4m/min
Limiting Pressure Velocity	0.100 MPa-m/sec @Pressure 1.75 MPa	2860 psi-ft/min @Pressure 254 psi	31.4 m/min

电气性能	额定值 (公制)	额定值 (英制)	测试方法
体积电阻率	1.00e+15 ohm-cm	1.00e+15 ohm-cm	IEC 60093:1980-01
表面电阻	1.00e+13 ohm	1.00e+13 ohm	IEC 60093:1980-01
介电常数	3.8 @Frequency 1.00e+6 Hz	3.8 @Frequency 1.00e+6 Hz
介电强度	16.5 kV/mm	419 kV/in	IEC 60243-1:1998-01
耗散因数	0.0050 @Frequency 100 Hz	0.0050 @Frequency 100 Hz	IEC 60250:1969-01
相比耐漏电起痕指数(CTI)	600 V	600 V	IEC 60112:2003-01

热性能	额定值 (公制)	额定值 (英制)	测试方法
线性热膨胀系数	92.0 μm/m-°C @Temperature 23.0 - 55.0 °C	51.1 μin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-2:1999
导热系数	0.310 W/m-K	2.15 BTU-in/hr-ft2-°F	Mean T=20°C; ISO 8301:1991
熔融温度	170 °C	338 °F
工作温度, Air	140 °C	284 °F	Intermittent
	90.0 °C @Time 1.80e+7 sec	194 °F @Time 5000 hour	Continuous
载荷下热变形温度(0.46 MPa)	160 °C	320 °F	ISO 75
载荷下热变形温度(1.8 MPa)	110 °C	230 °F	ISO 75
玻璃化转变温度，Tg	-60.0 °C	-76.0 °F	ISO 11359-2:1999
可燃性(UL94)	HB	HB

材料描述		测试方法
颜色	White/Black/Blue