PA 6巴斯夫 8202C 注塑级
- 品牌：巴斯夫
- 货号：A1900
- 价格： ￥15.2/千克
- 发布日期： 2022-11-04
- 更新日期： 2023-12-05
产品详请
| 品牌 | 巴斯夫 |
| 货号 | A1900 |
| 牌号 | 8202C |
| 型号 | 8202C |
| 品名 | PA6 |
| 外形尺寸 | 00.1 |
| 产品用途 | 车轮 汽车领域的应用 外壳 |
| 生产企业 | 73G15T |
| 是否进口 | 是 |
BASF Ultramid® 8202C PA6 (Conditioned)
Nylon 6, Unreinforced, Flame Retardant
BASF
产品说明：
Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique crystalline structure results in increased strength, stiffness, heat distortion temperature and performance under load as a homopolymer. It also cycles faster while maintaining properties and resistance.
物性信息：
物理性能
额定值 (公制)
额定值 (英制)
测试方法
密度
1.13 g/cc
0.0408 lb/in3
dry; ISO 1183
吸水率
1.6 %
1.6 %
24 hour; ISO Test
9.3 %
9.3 %
beginning dry; ISO 62
平衡吸湿
2.6 %
2.6 %
beginning dry (23°C/50% R.H.); ISO 62
Relative Viscosity
2.6 cP
2.6 cP
ISO Test; 96 % SAV
粘度测量
48
48
Formic Acid
线性成型收缩率
0.0090 cm/cm
0.0090 in/in
ASTM Data; MD
BASF Ultramid® 8202C PA6 (Conditioned)
Nylon 6, Unreinforced, Flame Retardant
BASF
产品说明：
Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique crystalline structure results in increased strength, stiffness, heat distortion temperature and performance under load as a homopolymer. It also cycles faster while maintaining properties and resistance.
物性信息：
物理性能
额定值 (公制)
额定值 (英制)
测试方法
密度
1.13 g/cc
0.0408 lb/in3
dry; ISO 1183
吸水率
1.6 %
1.6 %
24 hour; ISO Test
9.3 %
9.3 %
beginning dry; ISO 62
平衡吸湿
2.6 %
2.6 %
beginning dry (23°C/50% R.H.); ISO 62
Relative Viscosity
2.6 cP
2.6 cP
ISO Test; 96 % SAV
粘度测量
48
48
Formic Acid
线性成型收缩率
0.0090 cm/cm
0.0090 in/in
ASTM Data; MD
BASF Ultramid® 8202C PA6 (Conditioned)
Nylon 6, Unreinforced, Flame Retardant
BASF
产品说明：
Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique crystalline structure results in increased strength, stiffness, heat distortion temperature and performance under load as a homopolymer. It also cycles faster while maintaining properties and resistance.
物性信息：
物理性能
额定值 (公制)
额定值 (英制)
测试方法
密度
1.13 g/cc
0.0408 lb/in3
dry; ISO 1183
吸水率
1.6 %
1.6 %
24 hour; ISO Test
9.3 %
9.3 %
beginning dry; ISO 62
平衡吸湿
2.6 %
2.6 %
beginning dry (23°C/50% R.H.); ISO 62
Relative Viscosity
2.6 cP
2.6 cP
ISO Test; 96 % SAV
粘度测量
48
48
Formic Acid
线性成型收缩率
0.0090 cm/cm
0.0090 in/in
ASTM Data; MD
BASF Ultramid® 8202C PA6 (Conditioned)
Nylon 6, Unreinforced, Flame Retardant
BASF
产品说明：
Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique crystalline structure results in increased strength, stiffness, heat distortion temperature and performance under load as a homopolymer. It also cycles faster while maintaining properties and resistance.
物性信息：
物理性能
额定值 (公制)
额定值 (英制)
测试方法
密度
1.13 g/cc
0.0408 lb/in3
dry; ISO 1183
吸水率
1.6 %
1.6 %
24 hour; ISO Test
9.3 %
9.3 %
beginning dry; ISO 62
平衡吸湿
2.6 %
2.6 %
beginning dry (23°C/50% R.H.); ISO 62
Relative Viscosity
2.6 cP
2.6 cP
ISO Test; 96 % SAV
粘度测量
48
48
Formic Acid
线性成型收缩率
0.0090 cm/cm
0.0090 in/in
ASTM Data; MD
BASF Ultramid® 8202C PA6 (Conditioned)
Nylon 6, Unreinforced, Flame Retardant
BASF
产品说明：
Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique crystalline structure results in increased strength, stiffness, heat distortion temperature and performance under load as a homopolymer. It also cycles faster while maintaining properties and resistance.
物性信息：
物理性能
额定值 (公制)
额定值 (英制)
测试方法
密度
1.13 g/cc
0.0408 lb/in3
dry; ISO 1183
吸水率
1.6 %
1.6 %
24 hour; ISO Test
9.3 %
9.3 %
beginning dry; ISO 62
平衡吸湿
2.6 %
2.6 %
beginning dry (23°C/50% R.H.); ISO 62
Relative Viscosity
2.6 cP
2.6 cP
ISO Test; 96 % SAV
粘度测量
48
48
Formic Acid
线性成型收缩率
0.0090 cm/cm
0.0090 in/in
ASTM Data; MD
BASF Ultramid® 8202C PA6 (Conditioned)
Nylon 6, Unreinforced, Flame Retardant
BASF
产品说明：
Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique crystalline structure results in increased strength, stiffness, heat distortion temperature and performance under load as a homopolymer. It also cycles faster while maintaining properties and resistance.
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.13 g/cc | 0.0408 lb/in3 | dry; ISO 1183 |
| 吸水率 | 1.6 % | 1.6 % | 24 hour; ISO Test |
| 9.3 % | 9.3 % | beginning dry; ISO 62 | |
| 平衡吸湿 | 2.6 % | 2.6 % | beginning dry (23°C/50% R.H.); ISO 62 |
| Relative Viscosity | 2.6 cP | 2.6 cP | ISO Test; 96 % SAV |
| 粘度测量 | 48 | 48 | Formic Acid |
| 线性成型收缩率 | 0.0090 cm/cm | 0.0090 in/in | ASTM Data; MD |