增强材料PA6 巴斯夫 8231G HS 注塑级
- 品牌:巴斯夫
- 货号:A1900
- 价格: ¥15.2/千克
- 发布日期: 2022-11-04
- 更新日期: 2024-04-29
产品详请
品牌 | 巴斯夫 |
货号 | A1900 |
牌号 | 8231G HS |
型号 | 8231G HS |
品名 | PA6 |
外形尺寸 | 00.1 |
产品用途 | 保护性遮盖物 草坪和园林设备 插头 管件 紧固件 外壳 |
生产企业 | 73G15T |
是否进口 | 是 |
Ultramid® 8231G HS BK-102
Polyamide 6
BASF Corporation
14% 玻璃纤维增强材料
产品说明:
Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 15% glass fiber reinforced PA6 injection molding compound. The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons.
Applications
Ultramid 8231G HS BK-102 is ideally suited for more demanding performance applications such as safety helmet parts, washers, gears, engine and motor parts, chutes, and higher temperature environments.
物性信息:
基本信息
黄卡编号
-
E36632-231123
填料/增强材料
-
玻璃纤维增强材料, 14% 填料按重量
添加剂
-
热稳定剂
特性
-
半结晶
-
尺寸稳定性良好
-
低粘度
-
刚性,良好
-
高光
-
高强度
-
抗弯曲
-
可加工性,良好
-
良好的抗热老化性
-
良好的流动性
-
良好耐磨损性
-
耐化学性良好
-
热稳定性
-
热稳定性,良好
-
优良外观
用途
-
安全帽
-
齿轮
-
垫圈
-
汽车内部零件
机构评级
-
EC 1907/2006 (REACH)
RoHS 合规性
-
RoHS 合规
外观
-
黑色
形式
-
粒子
加工方法
-
注射成型
物理性能
干燥
调节后的
单位制
测试方法
比重
1.23
--
g/cm3
ASTM D792, ISO 1183
收缩率 - 流动 (3.18 mm)
0.50
--
%
吸水率
24 hr
1.4
--
%
ASTM D570
23°C, 24 hr
1.4
--
%
ISO 62
饱和
8.1
--
%
ASTM D570
饱和, 23°C
8.1
--
%
ISO 62
平衡, 50% RH
2.3
--
%
ASTM D570
平衡, 23°C, 50% RH
2.3
--
%
ISO 62
硬度
干燥
调节后的
单位制
测试方法
洛氏硬度 (R 级)
121
--
ASTM D785
机械性能
干燥
调节后的
单位制
测试方法
拉伸模量
ISO 527-2
-40°C
6880
6900
MPa
ISO 527-2
23°C
6130
3100
MPa
ISO 527-2
80°C
2450
2300
MPa
ISO 527-2
121°C
2020
1800
MPa
ISO 527-2
抗张强度
ASTM D638, ISO 527-2
断裂, -40°C
150
150
MPa
ASTM D638, ISO 527-2
断裂, 23°C
130
60.0
MPa
ASTM D638, ISO 527-2
断裂, 80°C
60.0
30.0
MPa
ASTM D638, ISO 527-2
断裂, 121°C
50.0
40.0
MPa
ASTM D638, ISO 527-2
伸长率
断裂, -40°C
3.0
3.0
%
ASTM D638
断裂, 23°C
3.0
20
%
ASTM D638, ISO 527-2
断裂, 80°C
14
15
%
ASTM D638
断裂, 121°C
10
9.0
%
ASTM D638
Ultramid® 8231G HS BK-102
Polyamide 6
BASF Corporation
14% 玻璃纤维增强材料
产品说明:
Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 15% glass fiber reinforced PA6 injection molding compound. The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons.
Applications
Ultramid 8231G HS BK-102 is ideally suited for more demanding performance applications such as safety helmet parts, washers, gears, engine and motor parts, chutes, and higher temperature environments.
物性信息:
基本信息
黄卡编号
-
E36632-231123
填料/增强材料
-
玻璃纤维增强材料, 14% 填料按重量
添加剂
-
热稳定剂
特性
-
半结晶
-
尺寸稳定性良好
-
低粘度
-
刚性,良好
-
高光
-
高强度
-
抗弯曲
-
可加工性,良好
-
良好的抗热老化性
-
良好的流动性
-
良好耐磨损性
-
耐化学性良好
-
热稳定性
-
热稳定性,良好
-
优良外观
用途
-
安全帽
-
齿轮
-
垫圈
-
汽车内部零件
机构评级
-
EC 1907/2006 (REACH)
RoHS 合规性
-
RoHS 合规
外观
-
黑色
形式
-
粒子
加工方法
-
注射成型
物理性能
干燥
调节后的
单位制
测试方法
比重
1.23
--
g/cm3
ASTM D792, ISO 1183
收缩率 - 流动 (3.18 mm)
0.50
--
%
吸水率
24 hr
1.4
--
%
ASTM D570
23°C, 24 hr
1.4
--
%
ISO 62
饱和
8.1
--
%
ASTM D570
饱和, 23°C
8.1
--
%
ISO 62
平衡, 50% RH
2.3
--
%
ASTM D570
平衡, 23°C, 50% RH
2.3
--
%
ISO 62
硬度
干燥
调节后的
单位制
测试方法
洛氏硬度 (R 级)
121
--
ASTM D785
机械性能
干燥
调节后的
单位制
测试方法
拉伸模量
ISO 527-2
-40°C
6880
6900
MPa
ISO 527-2
23°C
6130
3100
MPa
ISO 527-2
80°C
2450
2300
MPa
ISO 527-2
121°C
2020
1800
MPa
ISO 527-2
抗张强度
ASTM D638, ISO 527-2
断裂, -40°C
150
150
MPa
ASTM D638, ISO 527-2
断裂, 23°C
130
60.0
MPa
ASTM D638, ISO 527-2
断裂, 80°C
60.0
30.0
MPa
ASTM D638, ISO 527-2
断裂, 121°C
50.0
40.0
MPa
ASTM D638, ISO 527-2
伸长率
断裂, -40°C
3.0
3.0
%
ASTM D638
断裂, 23°C
3.0
20
%
ASTM D638, ISO 527-2
断裂, 80°C
14
15
%
ASTM D638
断裂, 121°C
10
9.0
%
ASTM D638
Ultramid® 8231G HS BK-102
Polyamide 6
BASF Corporation
14% 玻璃纤维增强材料
产品说明:
Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 15% glass fiber reinforced PA6 injection molding compound. The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons.
Applications
Ultramid 8231G HS BK-102 is ideally suited for more demanding performance applications such as safety helmet parts, washers, gears, engine and motor parts, chutes, and higher temperature environments.
物性信息:
基本信息
黄卡编号
-
E36632-231123
填料/增强材料
-
玻璃纤维增强材料, 14% 填料按重量
添加剂
-
热稳定剂
特性
-
半结晶
-
尺寸稳定性良好
-
低粘度
-
刚性,良好
-
高光
-
高强度
-
抗弯曲
-
可加工性,良好
-
良好的抗热老化性
-
良好的流动性
-
良好耐磨损性
-
耐化学性良好
-
热稳定性
-
热稳定性,良好
-
优良外观
用途
-
安全帽
-
齿轮
-
垫圈
-
汽车内部零件
机构评级
-
EC 1907/2006 (REACH)
RoHS 合规性
-
RoHS 合规
外观
-
黑色
形式
-
粒子
加工方法
-
注射成型
物理性能
干燥
调节后的
单位制
测试方法
比重
1.23
--
g/cm3
ASTM D792, ISO 1183
收缩率 - 流动 (3.18 mm)
0.50
--
%
吸水率
24 hr
1.4
--
%
ASTM D570
23°C, 24 hr
1.4
--
%
ISO 62
饱和
8.1
--
%
ASTM D570
饱和, 23°C
8.1
--
%
ISO 62
平衡, 50% RH
2.3
--
%
ASTM D570
平衡, 23°C, 50% RH
2.3
--
%
ISO 62
硬度
干燥
调节后的
单位制
测试方法
洛氏硬度 (R 级)
121
--
ASTM D785
机械性能
干燥
调节后的
单位制
测试方法
拉伸模量
ISO 527-2
-40°C
6880
6900
MPa
ISO 527-2
23°C
6130
3100
MPa
ISO 527-2
80°C
2450
2300
MPa
ISO 527-2
121°C
2020
1800
MPa
ISO 527-2
抗张强度
ASTM D638, ISO 527-2
断裂, -40°C
150
150
MPa
ASTM D638, ISO 527-2
断裂, 23°C
130
60.0
MPa
ASTM D638, ISO 527-2
断裂, 80°C
60.0
30.0
MPa
ASTM D638, ISO 527-2
断裂, 121°C
50.0
40.0
MPa
ASTM D638, ISO 527-2
伸长率
断裂, -40°C
3.0
3.0
%
ASTM D638
断裂, 23°C
3.0
20
%
ASTM D638, ISO 527-2
断裂, 80°C
14
15
%
ASTM D638
断裂, 121°C
10
9.0
%
ASTM D638
Ultramid® 8231G HS BK-102
Polyamide 6
BASF Corporation
14% 玻璃纤维增强材料
产品说明:
Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 15% glass fiber reinforced PA6 injection molding compound. The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons.
Applications
Ultramid 8231G HS BK-102 is ideally suited for more demanding performance applications such as safety helmet parts, washers, gears, engine and motor parts, chutes, and higher temperature environments.
物性信息:
基本信息
黄卡编号
-
E36632-231123
填料/增强材料
-
玻璃纤维增强材料, 14% 填料按重量
添加剂
-
热稳定剂
特性
-
半结晶
-
尺寸稳定性良好
-
低粘度
-
刚性,良好
-
高光
-
高强度
-
抗弯曲
-
可加工性,良好
-
良好的抗热老化性
-
良好的流动性
-
良好耐磨损性
-
耐化学性良好
-
热稳定性
-
热稳定性,良好
-
优良外观
用途
-
安全帽
-
齿轮
-
垫圈
-
汽车内部零件
机构评级
-
EC 1907/2006 (REACH)
RoHS 合规性
-
RoHS 合规
外观
-
黑色
形式
-
粒子
加工方法
-
注射成型
物理性能
干燥
调节后的
单位制
测试方法
比重
1.23
--
g/cm3
ASTM D792, ISO 1183
收缩率 - 流动 (3.18 mm)
0.50
--
%
吸水率
24 hr
1.4
--
%
ASTM D570
23°C, 24 hr
1.4
--
%
ISO 62
饱和
8.1
--
%
ASTM D570
饱和, 23°C
8.1
--
%
ISO 62
平衡, 50% RH
2.3
--
%
ASTM D570
平衡, 23°C, 50% RH
2.3
--
%
ISO 62
硬度
干燥
调节后的
单位制
测试方法
洛氏硬度 (R 级)
121
--
ASTM D785
机械性能
干燥
调节后的
单位制
测试方法
拉伸模量
ISO 527-2
-40°C
6880
6900
MPa
ISO 527-2
23°C
6130
3100
MPa
ISO 527-2
80°C
2450
2300
MPa
ISO 527-2
121°C
2020
1800
MPa
ISO 527-2
抗张强度
ASTM D638, ISO 527-2
断裂, -40°C
150
150
MPa
ASTM D638, ISO 527-2
断裂, 23°C
130
60.0
MPa
ASTM D638, ISO 527-2
断裂, 80°C
60.0
30.0
MPa
ASTM D638, ISO 527-2
断裂, 121°C
50.0
40.0
MPa
ASTM D638, ISO 527-2
伸长率
断裂, -40°C
3.0
3.0
%
ASTM D638
断裂, 23°C
3.0
20
%
ASTM D638, ISO 527-2
断裂, 80°C
14
15
%
ASTM D638
断裂, 121°C
10
9.0
%
ASTM D638
Ultramid® 8231G HS BK-102
Polyamide 6
BASF Corporation
14% 玻璃纤维增强材料
产品说明:
Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 15% glass fiber reinforced PA6 injection molding compound. The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons.
Applications
Ultramid 8231G HS BK-102 is ideally suited for more demanding performance applications such as safety helmet parts, washers, gears, engine and motor parts, chutes, and higher temperature environments.
物性信息:
基本信息
黄卡编号
-
E36632-231123
填料/增强材料
-
玻璃纤维增强材料, 14% 填料按重量
添加剂
-
热稳定剂
特性
-
半结晶
-
尺寸稳定性良好
-
低粘度
-
刚性,良好
-
高光
-
高强度
-
抗弯曲
-
可加工性,良好
-
良好的抗热老化性
-
良好的流动性
-
良好耐磨损性
-
耐化学性良好
-
热稳定性
-
热稳定性,良好
-
优良外观
用途
-
安全帽
-
齿轮
-
垫圈
-
汽车内部零件
机构评级
-
EC 1907/2006 (REACH)
RoHS 合规性
-
RoHS 合规
外观
-
黑色
形式
-
粒子
加工方法
-
注射成型
物理性能
干燥
调节后的
单位制
测试方法
比重
1.23
--
g/cm3
ASTM D792, ISO 1183
收缩率 - 流动 (3.18 mm)
0.50
--
%
吸水率
24 hr
1.4
--
%
ASTM D570
23°C, 24 hr
1.4
--
%
ISO 62
饱和
8.1
--
%
ASTM D570
饱和, 23°C
8.1
--
%
ISO 62
平衡, 50% RH
2.3
--
%
ASTM D570
平衡, 23°C, 50% RH
2.3
--
%
ISO 62
硬度
干燥
调节后的
单位制
测试方法
洛氏硬度 (R 级)
121
--
ASTM D785
机械性能
干燥
调节后的
单位制
测试方法
拉伸模量
ISO 527-2
-40°C
6880
6900
MPa
ISO 527-2
23°C
6130
3100
MPa
ISO 527-2
80°C
2450
2300
MPa
ISO 527-2
121°C
2020
1800
MPa
ISO 527-2
抗张强度
ASTM D638, ISO 527-2
断裂, -40°C
150
150
MPa
ASTM D638, ISO 527-2
断裂, 23°C
130
60.0
MPa
ASTM D638, ISO 527-2
断裂, 80°C
60.0
30.0
MPa
ASTM D638, ISO 527-2
断裂, 121°C
50.0
40.0
MPa
ASTM D638, ISO 527-2
伸长率
断裂, -40°C
3.0
3.0
%
ASTM D638
断裂, 23°C
3.0
20
%
ASTM D638, ISO 527-2
断裂, 80°C
14
15
%
ASTM D638
断裂, 121°C
10
9.0
%
ASTM D638
Ultramid® 8231G HS BK-102
Polyamide 6
BASF Corporation
14% 玻璃纤维增强材料
产品说明:
Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 15% glass fiber reinforced PA6 injection molding compound. The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons.
Applications
Ultramid 8231G HS BK-102 is ideally suited for more demanding performance applications such as safety helmet parts, washers, gears, engine and motor parts, chutes, and higher temperature environments.
物性信息:
基本信息
黄卡编号
-
E36632-231123
填料/增强材料
-
玻璃纤维增强材料, 14% 填料按重量
添加剂
-
热稳定剂
特性
-
半结晶
-
尺寸稳定性良好
-
低粘度
-
刚性,良好
-
高光
-
高强度
-
抗弯曲
-
可加工性,良好
-
良好的抗热老化性
-
良好的流动性
-
良好耐磨损性
-
耐化学性良好
-
热稳定性
-
热稳定性,良好
-
优良外观
用途
-
安全帽
-
齿轮
-
垫圈
-
汽车内部零件
机构评级
-
EC 1907/2006 (REACH)
RoHS 合规性
-
RoHS 合规
外观
-
黑色
形式
-
粒子
加工方法
-
注射成型
物理性能
干燥
调节后的
单位制
测试方法
比重
1.23
--
g/cm3
ASTM D792, ISO 1183
收缩率 - 流动 (3.18 mm)
0.50
--
%
吸水率
24 hr
1.4
--
%
ASTM D570
23°C, 24 hr
1.4
--
%
ISO 62
饱和
8.1
--
%
ASTM D570
饱和, 23°C
8.1
--
%
ISO 62
平衡, 50% RH
2.3
--
%
ASTM D570
平衡, 23°C, 50% RH
2.3
--
%
ISO 62
硬度
干燥
调节后的
单位制
测试方法
洛氏硬度 (R 级)
121
--
ASTM D785
机械性能
干燥
调节后的
单位制
测试方法
拉伸模量
ISO 527-2
-40°C
6880
6900
MPa
ISO 527-2
23°C
6130
3100
MPa
ISO 527-2
80°C
2450
2300
MPa
ISO 527-2
121°C
2020
1800
MPa
ISO 527-2
抗张强度
ASTM D638, ISO 527-2
断裂, -40°C
150
150
MPa
ASTM D638, ISO 527-2
断裂, 23°C
130
60.0
MPa
ASTM D638, ISO 527-2
断裂, 80°C
60.0
30.0
MPa
ASTM D638, ISO 527-2
断裂, 121°C
50.0
40.0
MPa
ASTM D638, ISO 527-2
伸长率
断裂, -40°C
3.0
3.0
%
ASTM D638
断裂, 23°C
3.0
20
%
ASTM D638, ISO 527-2
断裂, 80°C
14
15
%
ASTM D638
断裂, 121°C
10
9.0
%
ASTM D638
Ultramid® 8231G HS BK-102
Polyamide 6
BASF Corporation
14% 玻璃纤维增强材料
产品说明:
Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 15% glass fiber reinforced PA6 injection molding compound. The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons.
Applications
Ultramid 8231G HS BK-102 is ideally suited for more demanding performance applications such as safety helmet parts, washers, gears, engine and motor parts, chutes, and higher temperature environments.
物性信息:
基本信息
黄卡编号
-
E36632-231123
填料/增强材料
-
玻璃纤维增强材料, 14% 填料按重量
添加剂
-
热稳定剂
特性
-
半结晶
-
尺寸稳定性良好
-
低粘度
-
刚性,良好
-
高光
-
高强度
-
抗弯曲
-
可加工性,良好
-
良好的抗热老化性
-
良好的流动性
-
良好耐磨损性
-
耐化学性良好
-
热稳定性
-
热稳定性,良好
-
优良外观
用途
-
安全帽
-
齿轮
-
垫圈
-
汽车内部零件
机构评级
-
EC 1907/2006 (REACH)
RoHS 合规性
-
RoHS 合规
外观
-
黑色
形式
-
粒子
加工方法
-
注射成型
物理性能
干燥
调节后的
单位制
测试方法
比重
1.23
--
g/cm3
ASTM D792, ISO 1183
收缩率 - 流动 (3.18 mm)
0.50
--
%
吸水率
24 hr
1.4
--
%
ASTM D570
23°C, 24 hr
1.4
--
%
ISO 62
饱和
8.1
--
%
ASTM D570
饱和, 23°C
8.1
--
%
ISO 62
平衡, 50% RH
2.3
--
%
ASTM D570
平衡, 23°C, 50% RH
2.3
--
%
ISO 62
硬度
干燥
调节后的
单位制
测试方法
洛氏硬度 (R 级)
121
--
ASTM D785
机械性能
干燥
调节后的
单位制
测试方法
拉伸模量
ISO 527-2
-40°C
6880
6900
MPa
ISO 527-2
23°C
6130
3100
MPa
ISO 527-2
80°C
2450
2300
MPa
ISO 527-2
121°C
2020
1800
MPa
ISO 527-2
抗张强度
ASTM D638, ISO 527-2
断裂, -40°C
150
150
MPa
ASTM D638, ISO 527-2
断裂, 23°C
130
60.0
MPa
ASTM D638, ISO 527-2
断裂, 80°C
60.0
30.0
MPa
ASTM D638, ISO 527-2
断裂, 121°C
50.0
40.0
MPa
ASTM D638, ISO 527-2
伸长率
断裂, -40°C
3.0
3.0
%
ASTM D638
断裂, 23°C
3.0
20
%
ASTM D638, ISO 527-2
断裂, 80°C
14
15
%
ASTM D638
断裂, 121°C
10
9.0
%
ASTM D638
Ultramid® 8231G HS BK-102
Polyamide 6
BASF Corporation
14% 玻璃纤维增强材料
产品说明:
Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 15% glass fiber reinforced PA6 injection molding compound. The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons.
Applications
Ultramid 8231G HS BK-102 is ideally suited for more demanding performance applications such as safety helmet parts, washers, gears, engine and motor parts, chutes, and higher temperature environments.
物性信息:
基本信息
黄卡编号
-
E36632-231123
填料/增强材料
-
玻璃纤维增强材料, 14% 填料按重量
添加剂
-
热稳定剂
特性
-
半结晶
-
尺寸稳定性良好
-
低粘度
-
刚性,良好
-
高光
-
高强度
-
抗弯曲
-
可加工性,良好
-
良好的抗热老化性
-
良好的流动性
-
良好耐磨损性
-
耐化学性良好
-
热稳定性
-
热稳定性,良好
-
优良外观
用途
-
安全帽
-
齿轮
-
垫圈
-
汽车内部零件
机构评级
-
EC 1907/2006 (REACH)
RoHS 合规性
-
RoHS 合规
外观
-
黑色
形式
-
粒子
加工方法
-
注射成型
物理性能
干燥
调节后的
单位制
测试方法
比重
1.23
--
g/cm3
ASTM D792, ISO 1183
收缩率 - 流动 (3.18 mm)
0.50
--
%
吸水率
24 hr
1.4
--
%
ASTM D570
23°C, 24 hr
1.4
--
%
ISO 62
饱和
8.1
--
%
ASTM D570
饱和, 23°C
8.1
--
%
ISO 62
平衡, 50% RH
2.3
--
%
ASTM D570
平衡, 23°C, 50% RH
2.3
--
%
ISO 62
硬度
干燥
调节后的
单位制
测试方法
洛氏硬度 (R 级)
121
--
ASTM D785
机械性能
干燥
调节后的
单位制
测试方法
拉伸模量
ISO 527-2
-40°C
6880
6900
MPa
ISO 527-2
23°C
6130
3100
MPa
ISO 527-2
80°C
2450
2300
MPa
ISO 527-2
121°C
2020
1800
MPa
ISO 527-2
抗张强度
ASTM D638, ISO 527-2
断裂, -40°C
150
150
MPa
ASTM D638, ISO 527-2
断裂, 23°C
130
60.0
MPa
ASTM D638, ISO 527-2
断裂, 80°C
60.0
30.0
MPa
ASTM D638, ISO 527-2
断裂, 121°C
50.0
40.0
MPa
ASTM D638, ISO 527-2
伸长率
断裂, -40°C
3.0
3.0
%
ASTM D638
断裂, 23°C
3.0
20
%
ASTM D638, ISO 527-2
断裂, 80°C
14
15
%
ASTM D638
断裂, 121°C
10
9.0
%
ASTM D638
Ultramid® 8231G HS BK-102
Polyamide 6
BASF Corporation
14% 玻璃纤维增强材料
产品说明:
Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 15% glass fiber reinforced PA6 injection molding compound. The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons.
Applications
Ultramid 8231G HS BK-102 is ideally suited for more demanding performance applications such as safety helmet parts, washers, gears, engine and motor parts, chutes, and higher temperature environments.
物性信息:
基本信息
黄卡编号
-
E36632-231123
填料/增强材料
-
玻璃纤维增强材料, 14% 填料按重量
添加剂
-
热稳定剂
特性
-
半结晶
-
尺寸稳定性良好
-
低粘度
-
刚性,良好
-
高光
-
高强度
-
抗弯曲
-
可加工性,良好
-
良好的抗热老化性
-
良好的流动性
-
良好耐磨损性
-
耐化学性良好
-
热稳定性
-
热稳定性,良好
-
优良外观
用途
-
安全帽
-
齿轮
-
垫圈
-
汽车内部零件
机构评级
-
EC 1907/2006 (REACH)
RoHS 合规性
-
RoHS 合规
外观
-
黑色
形式
-
粒子
加工方法
-
注射成型
物理性能
干燥
调节后的
单位制
测试方法
比重
1.23
--
g/cm3
ASTM D792, ISO 1183
收缩率 - 流动 (3.18 mm)
0.50
--
%
吸水率
24 hr
1.4
--
%
ASTM D570
23°C, 24 hr
1.4
--
%
ISO 62
饱和
8.1
--
%
ASTM D570
饱和, 23°C
8.1
--
%
ISO 62
平衡, 50% RH
2.3
--
%
ASTM D570
平衡, 23°C, 50% RH
2.3
--
%
ISO 62
硬度
干燥
调节后的
单位制
测试方法
洛氏硬度 (R 级)
121
--
ASTM D785
机械性能
干燥
调节后的
单位制
测试方法
拉伸模量
ISO 527-2
-40°C
6880
6900
MPa
ISO 527-2
23°C
6130
3100
MPa
ISO 527-2
80°C
2450
2300
MPa
ISO 527-2
121°C
2020
1800
MPa
ISO 527-2
抗张强度
ASTM D638, ISO 527-2
断裂, -40°C
150
150
MPa
ASTM D638, ISO 527-2
断裂, 23°C
130
60.0
MPa
ASTM D638, ISO 527-2
断裂, 80°C
60.0
30.0
MPa
ASTM D638, ISO 527-2
断裂, 121°C
50.0
40.0
MPa
ASTM D638, ISO 527-2
伸长率
断裂, -40°C
3.0
3.0
%
ASTM D638
断裂, 23°C
3.0
20
%
ASTM D638, ISO 527-2
断裂, 80°C
14
15
%
ASTM D638
断裂, 121°C
10
9.0
%
ASTM D638
Ultramid® 8231G HS BK-102
Polyamide 6
BASF Corporation
14% 玻璃纤维增强材料
产品说明:
Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 15% glass fiber reinforced PA6 injection molding compound. The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons.
Applications
Ultramid 8231G HS BK-102 is ideally suited for more demanding performance applications such as safety helmet parts, washers, gears, engine and motor parts, chutes, and higher temperature environments.
Applications
Ultramid 8231G HS BK-102 is ideally suited for more demanding performance applications such as safety helmet parts, washers, gears, engine and motor parts, chutes, and higher temperature environments.
物性信息:
基本信息 | |
---|---|
黄卡编号 |
|
填料/增强材料 |
|
添加剂 |
|
特性 |
|
用途 |
|
机构评级 |
|
RoHS 合规性 |
|
外观 |
|
形式 |
|
加工方法 |
|
物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
---|---|---|---|---|
比重 | 1.23 | -- | g/cm3 | ASTM D792, ISO 1183 |
收缩率 - 流动 (3.18 mm) | 0.50 | -- | % | |
吸水率 | ||||
24 hr | 1.4 | -- | % | ASTM D570 |
23°C, 24 hr | 1.4 | -- | % | ISO 62 |
饱和 | 8.1 | -- | % | ASTM D570 |
饱和, 23°C | 8.1 | -- | % | ISO 62 |
平衡, 50% RH | 2.3 | -- | % | ASTM D570 |
平衡, 23°C, 50% RH | 2.3 | -- | % | ISO 62 |
硬度 | 干燥 | 调节后的 | 单位制 | 测试方法 |
---|---|---|---|---|
洛氏硬度 (R 级) | 121 | -- | ASTM D785 |
机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
---|---|---|---|---|
拉伸模量 | ISO 527-2 | |||
-40°C | 6880 | 6900 | MPa | ISO 527-2 |
23°C | 6130 | 3100 | MPa | ISO 527-2 |
80°C | 2450 | 2300 | MPa | ISO 527-2 |
121°C | 2020 | 1800 | MPa | ISO 527-2 |
抗张强度 | ASTM D638, ISO 527-2 | |||
断裂, -40°C | 150 | 150 | MPa | ASTM D638, ISO 527-2 |
断裂, 23°C | 130 | 60.0 | MPa | ASTM D638, ISO 527-2 |
断裂, 80°C | 60.0 | 30.0 | MPa | ASTM D638, ISO 527-2 |
断裂, 121°C | 50.0 | 40.0 | MPa | ASTM D638, ISO 527-2 |
伸长率 | ||||
断裂, -40°C | 3.0 | 3.0 | % | ASTM D638 |
断裂, 23°C | 3.0 | 20 | % | ASTM D638, ISO 527-2 |
断裂, 80°C | 14 | 15 | % | ASTM D638 |
断裂, 121°C | 10 | 9.0 | % | ASTM D638 |